Understanding the evolution of dislocation structures during plastic deformation is critical for predicting the mechanical performance of metallic materials. In this work, we applied in situ scanning electron microscopy/electron backscatter diffraction tensile testing combined with multifractal (MF) analysis to assess deformation-induced dislocation structure evolution in solution-annealed 304L stainless steel, both in its as-received and neutron-irradiated states (5.4 displacements per atom). T